1Cr17Mn6Ni5N
China GB GB/T 1220 (1992) GB/T 3280 (1992) GB/T 4237 (1992) GB/T 4239 (1991) GB/T 4356 (2002) 1Cr17Mn6Ni5N Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc and Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
Datasheet for:Steel Grades:Specialsteel:1Cr17Mn6Ni5N
Chemical composition(mass fraction)(wt.%) of the 1Cr17Mn6Ni5N
Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade 1Cr17Mn6Ni5N
Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition |
Brinell hardness (HBW) |
662 (≥) |
765 (≥) |
33 |
32 |
31 |
Solution and Aging, Annealing, Ausaging, Q+T,etc |
222 |
Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and |
Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
14 |
- |
- |
|
|
0.14 |
- |
|
116 |
752 |
- |
23.3 |
123 |
|
- |
|
731 |
- |
14 |
31.2 |
|
|
343 |
344 |
Heat treated : 1761°C - 1122°C
The material does not have direct Metallography properties.
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.