USA AMS SAE AMS 5525J (2007), SAE AMS 5726E (2008), SAE AMS 5731L (2006), SAE AMS 5732J (2006), SAE AMS 5734K (2006), SAE AMS 5735J (1974), SAE AMS 5736G (1974), SAE AMS 5737P (2006), SAE AMS 5810B (2008), SAE AMS 5853C (2006), SAE AMS 5858D (2009), SAE AMS 5895E (2009), SAE AMS 5804H (2013), SAE AMS 5805H (2012), A 286 Superalloys A286 is also widely used in the offshore oil and gas industry where the components are subject to high levels of heat and stress. and Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
Category | Class | Grade | Standard | Country | Application |
---|---|---|---|---|---|
Steel Grades | Superalloys | A 286 | AMS | USA | A286 is also widely used in the offshore oil and gas industry where the components are subject to high levels of heat and stress. |
C | Mn | P | S | Si | Cr | Ni | Mo | Ti | V | Al | B | Co | Cu |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
≤0.08 | ≤2.00 | ≤0.025 | ≤0.025 | ≤1.00 | 13.50 -16.00 | 24.00 -27.00 | 1.00 -1.50 | 1.90 -2.35 | 0.10 -0.50 | ≤0.35 | 0.0003 -0.010 | ≤1.00 | ≤0.50 |
Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
221 (≥) | 374 (≥) | 22 | 44 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 141 |
Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
---|---|---|---|---|---|---|---|
33 | - | - | 0.34 | - | |||
227 | 772 | - | 33.3 | 241 | - | ||
142 | - | 44 | 31.2 | 334 | 424 |
Heat treated : 1476°C - 1662°C
SAE AMS 5525J (2007) | Steel, Corrosion and Heat-Resistant, Sheet, Strip, and Plate 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V 1800 °F (982 °C) Solution Heat Treated | SAE-AMS-5525J-(2007).pdf |
SAE AMS 5726E (2008) | Steel, Corrosion and Heat-Resistant, Bars and Wire 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V 1800 °F (982 °C) Solution Heat Treated and Work-Strengthened Consumable Electrode Melted 200 ksi (1379 MPa) Tensile Strength | SAE-AMS-5726E-(2008).pdf |
SAE AMS 5731L (2006) | Steel, Corrosion and Heat-Resistant, Bars, Wire, Forgings, Tubing, and Rings 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Melted, 1800 °F (982 °C) Solution Heat Treated | SAE-AMS-5731L-(2006).pdf |
SAE AMS 5732J (2006) | Steel, Corrosion and Heat-Resistant, Bars, Wire, Forgings, Tubing, and Rings 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Melted 1800 °F (982 °C) Solution and Precipitation Heat Treated | SAE-AMS-5732J-(2006).pdf |
SAE AMS 5734K (2006) | Steel, Corrosion and Heat-Resistant, Bars, Wire, Forgings, and Tubing 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Melted, 1650 °F (899 °C) Solution Heat Treated | SAE-AMS-5734K-(2006).pdf |
SAE AMS 5735J (1974) | Steel Bars, Forgings, Tubing, And Rings, Corrosion And Heat resistant 15Cr-26Ni-1.3Mo-2.1Ti-0.3V 1800°F (982.2°C) Solution and Precipitaion Heat Treated | SAE-AMS-5735J-(1974).pdf |
SAE AMS 5736G (1974) | Steel Bars, Forgings, Tubing, and Rings, Corrosion and Heat Resistant 15Cr 26Ni 1.3Mo 2.1Ti 0.30V 1800°F (982°C) Solution Heat Treated | SAE-AMS-5736G-(1974).pdf |
SAE AMS 5737P (2006) | Steel, Corrosion and Heat-Resistant, Bars, Wire, Forgings, and Tubing 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Melted 1650 °F (899 °C) Solution and Precipitation Heat Treated | SAE-AMS-5737P-(2006).pdf |
SAE AMS 5810B (2008) | Steel, Corrosion and Heat Resistant, Flat Wire 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V 1800 °F (982 °C) Solution Heat Treated, Cold Drawn or Cold Rolled and Aged, Consumable Electrode Melted | SAE-AMS-5810B-(2008).pdf |
SAE AMS 5853C (2006) | Steel, Corrosion and Heat-Resistant, Bars and Wire 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Melted 1800 °F (982 °C) lösungsgeglüht and Work-Strengthened 160 ksi (1103 MPa) Tensile Strength | SAE-AMS-5853C-(2006).pdf |
SAE AMS 5858D (2009) | Steel, Corrosion and Heat Resistant, Sheet, Strip, and Plate 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Multiple Melted, 1800 °F (982 °C) Solution Heat Treated, Welding Grade Precipitation Hardenable | SAE-AMS-5858D-(2009).pdf |
SAE AMS 5895E (2009) | Steel, Corrosion and Heat-Resistant, Bars, Wire, Forgings, Tubing, and Rings 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Melted, 1750 °F (954 °C) Solution Heat Treated, Welding Grade Precipitation Hardenable | SAE-AMS-5895E-(2009).pdf |
SAE AMS 5804H (2013) | Steel, Corrosion and Heat-Resistant, Welding Wire 15Cr - 25.5Ni - 1.3Mo - 2.2Ti - 0.006B - 0.30V | SAE-AMS-5804H-(2013).pdf |
SAE AMS 5805H (2012) | Steel, Corrosion and Heat Resistant, Welding Wire 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.004B - 0.30V Vacuum Induction Melted, Environment Controlled Packaging | SAE-AMS-5805H-(2012).pdf |