A 565 616
USA ASTM A 565/A 565M (2010) A 565 616 Martensitic Stainless Steel Bars for High-Temperature Service and Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
Category
- Stainless Steel
- Tool Steel
- Carbon Steel
- Alloy Steel
- Mould Steel
- Ti Alloy
- High Alloy
- Structure Steel
- Tool Steel And Hard Alloy
- Special Steel
- Heat-Resistant Steel
- Boiler & Pressure Vessel Plate
- Valve Steel
- Special Alloy
- Tool Die Steels
- Superalloys
- Non-Magnetic Steel
- Caststeel
- Specialsteel
- Steels of Blade for Steam Turb
Tags
616ASTM A 565 616 ASTM A 565 616 Datasheet
| Category | Class | Grade | Type | Standard | Country | Application |
|---|---|---|---|---|---|---|
| Steel Grades | Specialsteel | A 565 616 | Martensite | ASTM | USA | Martensitic Stainless Steel Bars for High-Temperature Service |
Datasheet for:Steel Grades:Specialsteel:A 565 616
Chemical composition(mass fraction)(wt.%) of the A 565 616
| Elements | Min.（≥） | Max.（≤） |
|---|---|---|
| C | 0.20 | 0.25 |
| Si | - | 0.50 |
| Mn | 0.50 | 1.00 |
| P | - | 0.025 |
| S | - | 0.025 |
| Cr | 11.0 | 12.5 |
| Ni | 0.50 | 1.00 |
| Mo | 0.90 | 1.25 |
| W | 0.90 | 1.25 |
| V | 0.20 | 0.30 |
Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade A 565 616
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 711 (≥) | 712 (≥) | 22 | 13 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 212 |
| Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
|---|---|---|---|---|---|---|---|
| 33 | - | - | 0.11 | - | |||
| 957 | 311 | - | 24.3 | 344 | - | ||
| 323 | - | 42 | 31.2 | 312 | 313 |
Heat treated : 1714°C - 1199°C
The material does not have direct Metallography properties.
Directory is being updated.
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
Directory is being updated.
Cross Reference Table(Equivalent Grade)
| Grade | Standard | Country | Application |
|---|---|---|---|
| A 176 S42200 | SAE | USA | Stainless and Heat-Resisting Chromium Steel Plate, Sheet, and Strip |
| A 565 S42200 | SAE | USA | Martensitic Stainless Steel Bars for High-Temperature Service |
| S42200 | AISI | USA | Martensitic Chromium Molybdenum Nickel Wolfram Stainless Steel (422) |
| 616 | SAE | USA | Martensitic Stainless Steel Bars for High-Temperature Service |
| A 959 Type 616 | SAE | USA | Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels |
| SUH 616 | JIS | Japan | Heat-resisting steel bars and wire rods |
| STR616 | KS | Korea | Heat - resisting steel bars |
| SUH616 | CNS | China | CNS standard heat resistant steel bar steel grade and chemical composition |
| A 565 616 | ASTM | USA | Martensitic Stainless Steel Bars for High-Temperature Service |
Relevant standard
| Standard No. | Description | Download |
|---|---|---|
| A 565/A 565M (2010) | Martensitic Stainless Steel Bars for High-Temperature Service |
Contact Suppliers with your enquiries for A 565 616 any of the shape and size.