2.4982
Germany DIN 2.4982 The high-temperature and high-strength steel and 2.4982 Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
Germany DIN 2.4982 The high-temperature and high-strength steel and 2.4982 Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
Category | Type | Steel Grade | Standard | Country | Application |
---|---|---|---|---|---|
Steel Grades | Special Steel | 2.4982 | DIN | Germany | The high-temperature and high-strength steel |
1.4977 |
|||||
X40CoNi20-20 |
|||||
1.4978 |
|||||
X50CoCrNi20-20 |
|||||
1.4944 |
|||||
X6NiCrTiMoVB25-15-2/X5NiCrTi26-15 |
|||||
1.4980 |
|||||
X8CrNiMoNb16-16 |
|||||
1.4981 |
|||||
1.4984 |
Chemical composition(mass fraction)(wt.%) of the 2.4982
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | Co(%) | Al(%) | Ti(%) | Other(%) |
---|---|---|---|---|---|---|---|---|---|---|
Max 0.10 | Max 1.00 | Max 1.00 | Max 0.020 | Max 0.010 | 18.0-21.0 | 4.00-5.00 | 15.0-21.0 | 0.80-2.00 | 1.80-3.00 | Fe Max 5.00 |
Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade 2.4982
Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
673 (≥) | 989 (≥) | 14 | 14 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 433 |
Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
---|---|---|---|---|---|---|---|
32 | - | - | 0.11 | - | |||
777 | 812 | - | 31.3 | 422 | - | ||
168 | - | 43 | 44.2 | 412 | 212 |
Grade | Standard | Country | Application |
---|---|---|---|
2.4982 | DIN | Germany | The high-temperature and high-strength steel |