GMW10M-IR-C N700M-2
USA GM GMW 10-2011 GMW10M-IR-C N700M-2 Nodular iron is a cast iron with an as-cast structure containing graphite of a spheroidal or nodular shape. and Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
USA GM GMW 10-2011 GMW10M-IR-C N700M-2 Nodular iron is a cast iron with an as-cast structure containing graphite of a spheroidal or nodular shape. and Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
Category | Class | Grade | Standard | Country | Application |
---|---|---|---|---|---|
Steel Grades | Specialsteel | GMW10M-IR-C N700M-2 | GM | USA | Nodular iron is a cast iron with an as-cast structure containing graphite of a spheroidal or nodular shape. |
Chemical composition(mass fraction)(wt.%) of the GMW10M-IR-C N700M-2
Elements | Min.(≥) | Max.(≤) |
---|---|---|
C | 3.30 | 3.39 |
Mn | 0.2 | 1.00 |
Si | 1.80 | 2.70 |
P | - | 0.05 |
Cu | - | 0.70 |
S | - | 0.02 |
Cr | - | 0.10 |
Mg | 0.03 | 0.05 |
Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade GMW10M-IR-C N700M-2
Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
319 (≥) | 174 (≥) | 13 | 34 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 222 |
Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
---|---|---|---|---|---|---|---|
21 | - | - | 0.12 | - | |||
522 | 597 | - | 41.3 | 442 | - | ||
274 | - | 44 | 44.2 | 212 | 242 |
Grade | Standard | Country | Application |
---|---|---|---|
GMW10M-IR-C N700M-2 | GM | USA | Nodular iron is a cast iron with an as-cast structure containing graphite of a spheroidal or nodular shape. |
Standard No. | Description | Download |
---|---|---|
GMW 10-2011 | Nodular Cast Iron |