0Cr19Ni9N
This page provides 0Cr19Ni9N datasheet, 0Cr19Ni9N mechanical properties, chemical element 0Cr19Ni9N, technical specifications of 0Cr19Ni9N steel material properties. 0Cr19Ni9N performance specifications.
GBT 0Cr19Ni9N
| Category | Type | Steel Grade | Standard | Country | Application |
|---|---|---|---|---|---|
| Steel Grades | Special Alloy | 0Cr19Ni9N | GBT | China | Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components |
| 1.7909 |
|||||
| 1.8159 |
|||||
| GS-50CrV4 |
|||||
| Y1Cr18Ni9 |
|||||
| 1Cr18Ni9 |
|||||
| 1Cr18Mn10Ni5Mo3N |
|||||
| 1Cr17Ni7 |
|||||
| Y1Cr18Ni9Se |
|||||
| 1Cr17Mn6Ni5N |
|||||
| 1Cr18Mn8Ni5N |
Datasheet for:Steel Grades:Special Alloy:0Cr19Ni9N
Chemical composition(mass fraction)(wt.%) of the 0Cr19Ni9N
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | N(%) |
|---|---|---|---|---|---|---|---|
| Max 0.08 | Max 1.00 | Max 2.00 | max 0.035 | Max 0.030 | 18.00-20.00 | 7.00-10.50 | 0.10-0.25 |
Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade 0Cr19Ni9N
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 629 (≥) | 559 (≥) | 12 | 22 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 312 |
| Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
|---|---|---|---|---|---|---|---|
| 42 | - | - | 0.34 | - | |||
| 447 | 854 | - | 33.3 | 412 | - | ||
| 761 | - | 23 | 32.2 | 233 | 431 |
Heat treated : 1426°C - 1744°C
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
Directory is being updated.
Cross Reference Table(Equivalent Grade)
| Grade | Standard | Country | Application |
|---|---|---|---|
| 0Cr19Ni9N | GBT | China | Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components |