This page provides ASTM 1345 datasheet, ASTM 1345 mechanical properties, chemical element ASTM 1345, technical specifications of ASTM 1345 steel material properties. ASTM 1345 performance specifications.
Category | Class | Grade | Standard | Country | Application |
---|---|---|---|---|---|
Steel Grades | Carbon Steel | ASTM 1345 |
Chemical composition(mass fraction)(wt.%) of the ASTM 1345
C ≤ |
Si ≤ |
Mn ≤ |
P ≤ |
S ≤ |
Cr | Ni |
---|---|---|---|---|---|---|
0.43-0.48 | 0.15-0.35 | 1.6-1.9 | 0.035 | 0.04 | ||
Mo | Al | Cu | Nb | Ti | V | Ce |
N | Co | Pb | B | Other | ||
Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade ASTM 1345
Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
697 (≥) | 142 (≥) | 31 | 22 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 411 |
Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
---|---|---|---|---|---|---|---|
23 | - | - | 0.12 | - | |||
971 | 731 | - | 42.3 | 422 | - | ||
969 | - | 23 | 42.2 | 134 | 424 |
Grade | Standard | Country | Application |
---|---|---|---|
Y1Cr18Ni9 | GB | China | Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut |
1Cr18Ni9 | GB | China | High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts |
1Cr18Mn10Ni5Mo3N | GB | China | Of urea with good corrosion resistance, can produce urea corrosion of the equipment. |
1Cr17Ni7 | GB | China | High strength after cold forming. Used in railway vehicle, conveyor belt, bolt and nut, etc |
Y1Cr18Ni9Se | GB | China | Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws |
0Cr18Ni9 | GB | China | Seamless stainless steel tubes for boiler and heat exchanger |
00Cr19Ni10 | GB | China | Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts |
1Cr17Mn6Ni5N | GB | China | Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc |
1Cr18Mn8Ni5N | GB | China | Nickel steel, instead of 1cr18ni9 |
0Cr19Ni9N | GB | China | Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components |
0Cr19Ni10NbN | GB | China | Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES |
00Cr18Ni10N | GB | China | In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance |
1Cr18Ni12 | GB | China | Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading |
0Cr23Ni13 | GB | China | Corrosion resistance and heat resistance are better than 0cr19ni9 |
0Cr25Ni20 | GB | China | Oxidation resistance is better than 0cr23ni13. Mostly used as heat resistant steel |
0Cr17Ni12Mo2 | GB | China | Seamless stainless steel tubes for boiler and heat exchanger |
1Cr18Ni12Mo2Ti | GB | China | Seamless stainless steel tubes for boiler and heat exchanger |
0Cr18Ni12Mo2Ti | GB | China | Seamless stainless steel tubes for boiler and heat exchanger |
A-29 1025 | SAE | USA | General use carbon steel rod |
1025 | SAE | USA | These products have been used typically for use in fabrication of fittings, but usage is not limited to such applications. These products are not typically used for deep forming or cupping operations. |
Join Supplier: sales@steel-grades.comHaihong International Trade (HK) CO., Limited