AMS 4924

This page provides AMS 4924 datasheet, AMS 4924 mechanical properties, chemical element AMS 4924, technical specifications of AMS 4924 steel material properties. AMS 4924 performance specifications.

Category Class Grade Standard Country Application
Steel GradesCarbon Steel AMS 4924
Datasheet for:Steel Grades:Carbon Steel:AMS 4924

Chemical composition(mass fraction)(wt.%) of the AMS 4924

 

AISI 1010 steel, hot rolled bar, 19-32 mm (0.75-1.25 in) round or thickness
Categories: Metal; Ferrous Metal; Carbon Steel; AISI 1000 Series Steel; Low Carbon steel
Material Notes: Easily cold formed by heading, extruding, upsetting, bending, and other deforming processes. Uses for wires include electroplated products, such as racks, storage bins, shopping carts, fan guards, and jewelry, and unplated such as wires, staples, hardware, and barbed wire.
Key Words: UNS G10100, AMS 5040, AMS 5042, AMS 5044, AMS 5047, AMS 5053, ASTM A29, ASTM A108, ASTM A510, ASTM A519, ASTM A545, ASTM A549, ASTM A575, ASTM A576, MIL SPEC MIL-S-11310 (CS1010), JIS S 9 CK, SAE J403, SAE J412, SAE J414, DIN 1.1121, AFNOR XC 10 (Fr), JIS S10 C, JIS S 12 C

 

 

Physical Properties Metric English Comments
Density  7.87 g/cc 0.284 lb/in³ Typical for steel
 
Mechanical Properties Metric English Comments
Hardness, Brinell  95 95
Hardness, Knoop  113 113 Converted from Brinell hardness.
Hardness, Rockwell B  55 55 Converted from Brinell hardness.
Hardness, Vickers  98 98 Converted from Brinell hardness.
Tensile Strength, Ultimate  325 MPa 47100 psi
Tensile Strength, Yield  180 MPa 26100 psi
Elongation at Break  28.0 % 28.0 % in 50 mm
Reduction of Area  50.0 % 50.0 %
Modulus of Elasticity  200 GPa 29000 ksi Typical for steel
Bulk Modulus  140 GPa 20300 ksi Typical for steel
Poissons Ratio  0.290 0.290 Typical For Steel
Machinability  55 % 55 % Based on AISI 1212 steel. as 100% machinability. The machinability of Group I bar, rod, and wire products can be improved by cold drawing.
Shear Modulus  80.0 GPa 11600 ksi Typical for steel
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.0000143 ohm-cm 0.0000143 ohm-cm condition unknown
 
Thermal Properties Metric English Comments
CTE, linear 12.2 µm/m-°C
@Temperature 0.000 - 100 °C
6.78 µin/in-°F
@Temperature 32.0 - 212 °F
  13.0 µm/m-°C
@Temperature 0.000 - 200 °C
7.22 µin/in-°F
@Temperature 32.0 - 392 °F
  13.5 µm/m-°C
@Temperature 0.000 - 300 °C
7.50 µin/in-°F
@Temperature 32.0 - 572 °F
  13.8 µm/m-°C
@Temperature 0.000 - 400 °C
7.67 µin/in-°F
@Temperature 32.0 - 752 °F
  14.2 µm/m-°C
@Temperature 0.000 - 500 °C
7.89 µin/in-°F
@Temperature 32.0 - 932 °F
  14.6 µm/m-°C
@Temperature 0.000 - 600 °C
8.11 µin/in-°F
@Temperature 32.0 - 1110 °F
  14.9 µm/m-°C
@Temperature 0.000 - 700 °C
8.28 µin/in-°F
@Temperature 32.0 - 1290 °F
Specific Heat Capacity  0.448 J/g-°C 0.107 BTU/lb-°F condition unknown; 50-100°C (122-212°F)
  0.498 J/g-°C
@Temperature 150 - 200 °C
0.119 BTU/lb-°F
@Temperature 302 - 392 °F
  0.519 J/g-°C
@Temperature 200 - 250 °C
0.124 BTU/lb-°F
@Temperature 392 - 482 °F
  0.536 J/g-°C
@Temperature 250 - 300 °C
0.128 BTU/lb-°F
@Temperature 482 - 572 °F
  0.565 J/g-°C
@Temperature 300 - 350 °C
0.135 BTU/lb-°F
@Temperature 572 - 662 °F
  0.590 J/g-°C
@Temperature 350 - 400 °C
0.141 BTU/lb-°F
@Temperature 662 - 752 °F
  0.649 J/g-°C
@Temperature 400 - 450 °C
0.155 BTU/lb-°F
@Temperature 752 - 842 °F
  0.729 J/g-°C
@Temperature 550 - 600 °C
0.174 BTU/lb-°F
@Temperature 1020 - 1110 °F
  0.825 J/g-°C
@Temperature 650 - 700 °C
0.197 BTU/lb-°F
@Temperature 1200 - 1290 °F
Thermal Conductivity  51.9 W/m-K 360 BTU-in/hr-ft²-°F Typical steel
 
Component Elements Properties Metric English Comments
Carbon, C  0.080 - 0.13 % 0.080 - 0.13 %
Iron, Fe  99.18 - 99.62 % 99.18 - 99.62 % As remainder
Manganese, Mn  0.30 - 0.60 % 0.30 - 0.60 %
Phosphorous, P  <= 0.040 % <= 0.040 %
Sulfur, S  <= 0.050 % <= 0.050 %

Users viewing this material also viewed the following:
AISI 1010 Steel, cold drawn
AISI 1010 Steel, cold drawn bar, 19-32 mm (0.75-1.25 in) round or thickness
AISI 1010 Steel, CQ sheet,1.6-5.8 mm round or thickness
AISI 1008 Steel, hot rolled bar, 19-32 mm (0.75-1.25 in) round
AISI 1008 Steel, cold drawn bar, 19-32 mm (0.75-1.25 in) round

M1010B / 6783

Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade AMS 4924

Yield
Rp0.2 (MPa)
Tensile
Rm (MPa)
Impact
KV/Ku (J)
Elongation
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
826 (≥) 631 (≥) 34 22 31 Solution and Aging, Annealing, Ausaging, Q+T,etc 343
Temperature
(°C)
Modulus of elasticity
(GPa)
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and Thermal conductivity
(W/m·°C)
Specific thermal capacity
(J/kg·°C)
Specific electrical resistivity
(Ω mm²/m)
Density
(kg/dm³)
Poisson’s coefficient, ν
12 - -     0.32 -  
768 865 - 42.3 112   -  
319 - 42 33.2   121 333
Heat treated : 1216°C - 1535°C
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
Cross Reference Table(Equivalent Grade)
Grade Standard Country Application
Y1Cr18Ni9 GB China
Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut
1Cr18Ni9 GB China
High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts
1Cr18Mn10Ni5Mo3N GB China
Of urea with good corrosion resistance, can produce urea corrosion of the equipment.
1Cr17Ni7 GB China
High strength after cold forming. Used in railway vehicle, conveyor belt, bolt and nut, etc
Y1Cr18Ni9Se GB China
Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws
0Cr18Ni9 GB China
Seamless stainless steel tubes for boiler and heat exchanger
00Cr19Ni10 GB China
Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts
1Cr17Mn6Ni5N GB China
Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc
1Cr18Mn8Ni5N GB China
Nickel steel, instead of 1cr18ni9
0Cr19Ni9N GB China
Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components
0Cr19Ni10NbN GB China
Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES
00Cr18Ni10N GB China
In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance
1Cr18Ni12 GB China
Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading
0Cr23Ni13 GB China
Corrosion resistance and heat resistance are better than 0cr19ni9
0Cr25Ni20 GB China
Oxidation resistance is better than 0cr23ni13. Mostly used as heat resistant steel
0Cr17Ni12Mo2 GB China
Seamless stainless steel tubes for boiler and heat exchanger
1Cr18Ni12Mo2Ti GB China
Seamless stainless steel tubes for boiler and heat exchanger
0Cr18Ni12Mo2Ti GB China
Seamless stainless steel tubes for boiler and heat exchanger
A-29 1025 SAE USA
General use carbon steel rod
1025 SAE USA
These products have been used typically for use in fabrication of fittings, but usage is not limited to such applications. These products are not typically used for deep forming or cupping operations.
AMS 4924 Suppliers

Haihong International Trade (HK) CO., Limited

Stainless Steel, Special Steel, Compressor Blading, Turbine Blading, Superalloy Supplier.
AMS 4924 can be supplied as steel plate/ sheet, round steel bar, steel tube/pipe, steel stripe, steel billet, steel ingot, steel wire rods. electroslag, forged ring/ block,etc.