This page provides AISI A3130 datasheet, AISI A3130 mechanical properties, chemical element AISI A3130, technical specifications of AISI A3130 steel material properties. AISI A3130 performance specifications.
Category | Class | Grade | Standard | Country | Application |
---|---|---|---|---|---|
Steel Grades | Carbon Steel | AISI A3130 |
Chemical composition(mass fraction)(wt.%) of the AISI A3130
C ≤ |
Si ≤ |
Mn ≤ |
P ≤ |
S ≤ |
Cr | Ni |
---|---|---|---|---|---|---|
0.28-0.33 | 0.2-0.35 | 0.6-0.8 | 0.04 | 0.04 | 0.55-0.75 | 1.1-1.4 |
Mo | Al | Cu | Nb | Ti | V | Ce |
N | Co | Pb | B | Other | ||
Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade AISI A3130
Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
442 (≥) | 385 (≥) | 12 | 12 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 332 |
Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
---|---|---|---|---|---|---|---|
32 | - | - | 0.21 | - | |||
189 | 492 | - | 32.3 | 133 | - | ||
588 | - | 11 | 44.2 | 243 | 411 |
Grade | Standard | Country | Application |
---|---|---|---|
A-2 | AISI | USA | Applied to the thermosetting plastic mold, the hardened mould as a whole |
Y1Cr18Ni9 | GB | China | Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut |
1Cr18Ni9 | GB | China | High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts |
1Cr18Mn10Ni5Mo3N | GB | China | Of urea with good corrosion resistance, can produce urea corrosion of the equipment. |
1Cr17Ni7 | GB | China | High strength after cold forming. Used in railway vehicle, conveyor belt, bolt and nut, etc |
Y1Cr18Ni9Se | GB | China | Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws |
0Cr18Ni9 | GB | China | Seamless stainless steel tubes for boiler and heat exchanger |
00Cr19Ni10 | GB | China | Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts |
1Cr17Mn6Ni5N | GB | China | Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc |
1Cr18Mn8Ni5N | GB | China | Nickel steel, instead of 1cr18ni9 |
0Cr19Ni9N | GB | China | Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components |
0Cr19Ni10NbN | GB | China | Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES |
00Cr18Ni10N | GB | China | In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance |
1Cr18Ni12 | GB | China | Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading |
0Cr23Ni13 | GB | China | Corrosion resistance and heat resistance are better than 0cr19ni9 |
0Cr25Ni20 | GB | China | Oxidation resistance is better than 0cr23ni13. Mostly used as heat resistant steel |
0Cr17Ni12Mo2 | GB | China | Seamless stainless steel tubes for boiler and heat exchanger |
1Cr18Ni12Mo2Ti | GB | China | Seamless stainless steel tubes for boiler and heat exchanger |
0Cr18Ni12Mo2Ti | GB | China | Seamless stainless steel tubes for boiler and heat exchanger |
A-29 1025 | SAE | USA | General use carbon steel rod |
Join Supplier: sales@steel-grades.comHaihong International Trade (HK) CO., Limited