SAE J403

This page provides SAE J403 datasheet, SAE J403 mechanical properties, chemical element SAE J403, technical specifications of SAE J403 steel material properties. SAE J403 performance specifications.

Category Class Grade Standard Country Application
Steel GradesCarbon Steel SAE J403
Datasheet for:Steel Grades:Carbon Steel:SAE J403

Chemical composition(mass fraction)(wt.%) of the SAE J403

Categories: Metal; Ferrous Metal; Carbon Steel; AISI 1000 Series Steel; Low Carbon steel

Material Notes: AISI 1005 Low Carbon steel

Key Words: UNS G10050, ASTM A29, ASTM A510, MIL SPEC MIL-S-11310 (CS1005), SAE J403, SAE J412

 

 

Physical Properties Metric English Comments
Density  7.872 g/cc 0.2844 lb/in³ Composition 0.06% C, 0.38% Mn, 0.01% Si, annealed at 925°C
 
Mechanical Properties Metric English Comments
Modulus of Elasticity  200 GPa 29000 ksi Typical for steel
Bulk Modulus  140 GPa 20300 ksi Typical for steel
Poissons Ratio  0.290 0.290 Typical For steel
Shear Modulus  80.0 GPa 11600 ksi Typical for steel
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.0000174 ohm-cm 0.0000174 ohm-cm Typical steel
 
Thermal Properties Metric English Comments
CTE, linear 12.6 µm/m-°C
@Temperature 0.000 - 100 °C
7.00 µin/in-°F
@Temperature 32.0 - 212 °F
  13.1 µm/m-°C
@Temperature 0.000 - 200 °C
7.28 µin/in-°F
@Temperature 32.0 - 392 °F
  13.5 µm/m-°C
@Temperature 0.000 - 300 °C
7.50 µin/in-°F
@Temperature 32.0 - 572 °F
  13.7 µm/m-°C
@Temperature 0.000 - 400 °C
7.61 µin/in-°F
@Temperature 32.0 - 752 °F
  13.7 µm/m-°C
@Temperature 0.000 - 1000 °C
7.61 µin/in-°F
@Temperature 32.0 - 1830 °F
  14.2 µm/m-°C
@Temperature 0.000 - 500 °C
7.89 µin/in-°F
@Temperature 32.0 - 932 °F
  14.6 µm/m-°C
@Temperature 0.000 - 600 °C
8.11 µin/in-°F
@Temperature 32.0 - 1110 °F
  14.9 µm/m-°C
@Temperature 0.000 - 700 °C
8.28 µin/in-°F
@Temperature 32.0 - 1290 °F
  16.6 µm/m-°C
@Temperature 0.000 - 800 °C
9.22 µin/in-°F
@Temperature 32.0 - 1470 °F
Specific Heat Capacity  0.481 J/g-°C 0.115 BTU/lb-°F 50-100°C (122-212°F)
  0.519 J/g-°C
@Temperature 150 - 200 °C
0.124 BTU/lb-°F
@Temperature 302 - 392 °F
  0.536 J/g-°C
@Temperature 200 - 250 °C
0.128 BTU/lb-°F
@Temperature 392 - 482 °F
  0.553 J/g-°C
@Temperature 250 - 300 °C
0.132 BTU/lb-°F
@Temperature 482 - 572 °F
  0.595 J/g-°C
@Temperature 350 - 400 °C
0.142 BTU/lb-°F
@Temperature 662 - 752 °F
  0.662 J/g-°C
@Temperature 450 - 500 °C
0.158 BTU/lb-°F
@Temperature 842 - 932 °F
  0.754 J/g-°C
@Temperature 550 - 600 °C
0.180 BTU/lb-°F
@Temperature 1020 - 1110 °F
  0.846 J/g-°C
@Temperature 850 - 900 °C
0.202 BTU/lb-°F
@Temperature 1560 - 1650 °F
  0.867 J/g-°C
@Temperature 650 - 700 °C
0.207 BTU/lb-°F
@Temperature 1200 - 1290 °F
  1.105 J/g-°C
@Temperature 700 - 750 °C
0.2641 BTU/lb-°F
@Temperature 1290 - 1380 °F
 
Component Elements Properties Metric English Comments
Carbon, C  <= 0.060 % <= 0.060 %
Iron, Fe  99.5 - 100 % 99.5 - 100 % As remainder
Manganese, Mn  <= 0.35 % <= 0.35 %
Phosphorous, P  <= 0.040 % <= 0.040 %
Sulfur, S  <= 0.050 % <= 0.050 %

Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade SAE J403

Yield
Rp0.2 (MPa)
Tensile
Rm (MPa)
Impact
KV/Ku (J)
Elongation
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
949 (≥) 263 (≥) 23 13 32 Solution and Aging, Annealing, Ausaging, Q+T,etc 422
Temperature
(°C)
Modulus of elasticity
(GPa)
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and Thermal conductivity
(W/m·°C)
Specific thermal capacity
(J/kg·°C)
Specific electrical resistivity
(Ω mm²/m)
Density
(kg/dm³)
Poisson’s coefficient, ν
22 - -     0.33 -  
827 163 - 44.3 322   -  
698 - 33 22.2   224 121
Heat treated : 1887°C - 1832°C
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
Cross Reference Table(Equivalent Grade)
Grade Standard Country Application
Y1Cr18Ni9 GB China
Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut
1Cr18Ni9 GB China
High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts
1Cr18Mn10Ni5Mo3N GB China
Of urea with good corrosion resistance, can produce urea corrosion of the equipment.
1Cr17Ni7 GB China
High strength after cold forming. Used in railway vehicle, conveyor belt, bolt and nut, etc
Y1Cr18Ni9Se GB China
Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws
0Cr18Ni9 GB China
Seamless stainless steel tubes for boiler and heat exchanger
00Cr19Ni10 GB China
Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts
1Cr17Mn6Ni5N GB China
Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc
1Cr18Mn8Ni5N GB China
Nickel steel, instead of 1cr18ni9
0Cr19Ni9N GB China
Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components
0Cr19Ni10NbN GB China
Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES
00Cr18Ni10N GB China
In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance
1Cr18Ni12 GB China
Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading
0Cr23Ni13 GB China
Corrosion resistance and heat resistance are better than 0cr19ni9
0Cr25Ni20 GB China
Oxidation resistance is better than 0cr23ni13. Mostly used as heat resistant steel
0Cr17Ni12Mo2 GB China
Seamless stainless steel tubes for boiler and heat exchanger
1Cr18Ni12Mo2Ti GB China
Seamless stainless steel tubes for boiler and heat exchanger
0Cr18Ni12Mo2Ti GB China
Seamless stainless steel tubes for boiler and heat exchanger
A-29 1025 SAE USA
General use carbon steel rod
1025 SAE USA
These products have been used typically for use in fabrication of fittings, but usage is not limited to such applications. These products are not typically used for deep forming or cupping operations.
SAE J403 Suppliers

Haihong International Trade (HK) CO., Limited

Stainless Steel, Special Steel, Compressor Blading, Turbine Blading, Superalloy Supplier.
SAE J403 can be supplied as steel plate/ sheet, round steel bar, steel tube/pipe, steel stripe, steel billet, steel ingot, steel wire rods. electroslag, forged ring/ block,etc.