ASTM A36

This page provides ASTM A36 datasheet, ASTM A36 mechanical properties, chemical element ASTM A36, technical specifications of ASTM A36 steel material properties. ASTM A36 performance specifications.

Category Class Grade Standard Country Application
Steel GradesCarbon Steel ASTM A36
Datasheet for:Steel Grades:Carbon Steel:ASTM A36

Chemical composition(mass fraction)(wt.%) of the ASTM A36

ASTM A36, >8 to 15 in. thick, as-rolled steel plate

Categories: Metal; Ferrous Metal; ASTM Steel; Carbon Steel; Low Carbon steel

Material Notes: A popular "workhorse" grade, it is used widely for various applications.
 

 

 

Physical Properties Metric English Comments
Density  7.85 g/cc 0.284 lb/in³ Typical of ASTM steel
 
Mechanical Properties Metric English Comments
Hardness, Brinell  119 - 159 119 - 159 based on conversion from tensile strength
Hardness, Rockwell B  67.0 - 83.0 67.0 - 83.0 based on conversion from tensile strength
Tensile Strength at Break  400 - 552 MPa 58000 - 80000 psi
Tensile Strength, Yield  >= 221 MPa >= 32000 psi
Elongation at Break  >= 18.0 % >= 18.0 % in 8"
  >= 21.0 % >= 21.0 % in 2", > 24" W
Bend Radius, Minimum  0.500 t 0.500 t ≤3/4" W; ASTM A6 PARA. S14
  1.00 t 1.00 t >3/4 to 1" W; ASTM A6 PARA. S14
  1.50 t 1.50 t >1 to 1-1/2" W; ASTM A6 PARA. S14
  2.50 t 2.50 t >1-1/2 to 2" W; ASTM A6 PARA. S14
  3.00 t 3.00 t >2" W; ASTM A6 PARA. S14
 
Component Elements Properties Metric English Comments
Carbon, C  <= 0.290 % <= 0.290 %
Copper, Cu  >= 0.020 % >= 0.020 %
Iron, Fe  >= 98.0 % >= 98.0 %
Manganese, Mn  0.85 - 1.20 % 0.85 - 1.20 %
Phosphorous, P  <= 0.040 % <= 0.040 %
Silicon, Si  0.15 - 0.40 % 0.15 - 0.40 %
Sulfur, S  <= 0.050 % <= 0.050 %

Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade ASTM A36

Yield
Rp0.2 (MPa)
Tensile
Rm (MPa)
Impact
KV/Ku (J)
Elongation
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
572 (≥) 696 (≥) 14 44 42 Solution and Aging, Annealing, Ausaging, Q+T,etc 433
Temperature
(°C)
Modulus of elasticity
(GPa)
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and Thermal conductivity
(W/m·°C)
Specific thermal capacity
(J/kg·°C)
Specific electrical resistivity
(Ω mm²/m)
Density
(kg/dm³)
Poisson’s coefficient, ν
14 - -     0.11 -  
331 133 - 23.3 212   -  
194 - 41 34.2   432 331
Heat treated : 1838°C - 1716°C
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
Cross Reference Table(Equivalent Grade)
Grade Standard Country Application
Y1Cr18Ni9 GB China
Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut
1Cr18Ni9 GB China
High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts
1Cr18Mn10Ni5Mo3N GB China
Of urea with good corrosion resistance, can produce urea corrosion of the equipment.
1Cr17Ni7 GB China
High strength after cold forming. Used in railway vehicle, conveyor belt, bolt and nut, etc
Y1Cr18Ni9Se GB China
Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws
0Cr18Ni9 GB China
Seamless stainless steel tubes for boiler and heat exchanger
00Cr19Ni10 GB China
Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts
1Cr17Mn6Ni5N GB China
Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc
1Cr18Mn8Ni5N GB China
Nickel steel, instead of 1cr18ni9
0Cr19Ni9N GB China
Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components
0Cr19Ni10NbN GB China
Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES
00Cr18Ni10N GB China
In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance
1Cr18Ni12 GB China
Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading
0Cr23Ni13 GB China
Corrosion resistance and heat resistance are better than 0cr19ni9
0Cr25Ni20 GB China
Oxidation resistance is better than 0cr23ni13. Mostly used as heat resistant steel
0Cr17Ni12Mo2 GB China
Seamless stainless steel tubes for boiler and heat exchanger
1Cr18Ni12Mo2Ti GB China
Seamless stainless steel tubes for boiler and heat exchanger
0Cr18Ni12Mo2Ti GB China
Seamless stainless steel tubes for boiler and heat exchanger
A-29 1025 SAE USA
General use carbon steel rod
1025 SAE USA
These products have been used typically for use in fabrication of fittings, but usage is not limited to such applications. These products are not typically used for deep forming or cupping operations.
ASTM A36 Suppliers

Haihong International Trade (HK) CO., Limited

Stainless Steel, Special Steel, Compressor Blading, Turbine Blading, Superalloy Supplier.
ASTM A36 can be supplied as steel plate/ sheet, round steel bar, steel tube/pipe, steel stripe, steel billet, steel ingot, steel wire rods. electroslag, forged ring/ block,etc.