AISI 1018 AISI 1018 Datasheet
Category Type Steel Grade Standard Country Application
Steel GradesCarbon Steel AISI 1018
SAE 1015
AISI 1015
UNS G10150
SAE 1016
AISI 1016
UNS G10160
SAE 1017
AISI 1017
UNS G10170
SAE 1018
Datasheet for:Steel Grades:Carbon Steel:AISI 1018

Chemical composition(mass fraction)(wt.%) of the AISI 1018

 

C
Si
Mn
P
S
Cr Ni
 0.15-0.2 0.07-0.6(a,b)  0.6-0.9  0.03  0.05     
Mo Al Cu Nb Ti V Ce
             
N Co Pb B Other    
             
             

Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade AISI 1018

Yield
Rp0.2 (MPa)
Tensile
Rm (MPa)
Impact
KV/Ku (J)
Elongation
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
171 (≥) 864 (≥) 44 11 31 Solution and Aging, Annealing, Ausaging, Q+T,etc 124
Temperature
(°C)
Modulus of elasticity
(GPa)
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and Thermal conductivity
(W/m·°C)
Specific thermal capacity
(J/kg·°C)
Specific electrical resistivity
(Ω mm²/m)
Density
(kg/dm³)
Poisson’s coefficient, ν
24 - -     0.42 -  
912 751 - 24.3 221   -  
868 - 44 41.2   312 431
Heat treated : 1717°C - 1854°C
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
Cross Reference Table(Equivalent Grade)
Grade Standard Country Application
A-2
Applied to the thermosetting plastic mold, the hardened mould as a whole
Y1Cr18Ni9
Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut
1Cr18Ni9
High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts
1Cr18Mn10Ni5Mo3N
Of urea with good corrosion resistance, can produce urea corrosion of the equipment.
1Cr17Ni7
High strength after cold forming. Used in railway vehicle, conveyor belt, bolt and nut, etc
Y1Cr18Ni9Se
Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws
0Cr18Ni9
Seamless stainless steel tubes for boiler and heat exchanger
00Cr19Ni10
Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts
1Cr17Mn6Ni5N
Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc
1Cr18Mn8Ni5N
Nickel steel, instead of 1cr18ni9
0Cr19Ni9N
Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components
0Cr19Ni10NbN
Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES
00Cr18Ni10N
In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance
1Cr18Ni12
Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading
0Cr23Ni13
Corrosion resistance and heat resistance are better than 0cr19ni9
0Cr25Ni20
Oxidation resistance is better than 0cr23ni13. Mostly used as heat resistant steel
0Cr17Ni12Mo2
Seamless stainless steel tubes for boiler and heat exchanger
1Cr18Ni12Mo2Ti
Seamless stainless steel tubes for boiler and heat exchanger
0Cr18Ni12Mo2Ti
Seamless stainless steel tubes for boiler and heat exchanger
A-29 1025
General use carbon steel rod